Two-Component Tin Cure Liquid Silicone Rubber DIY Crafts Mold High Strength with Easy Perfusion Industrial Use
Description of Tin Cure Silicone Rubber
HN-620 A/B is a two-component liquid silicone material. Two components are mixed in a ratio of 100:2. This product is cured at room temperature.
Application of Tin Cure Silicone Rubber
HN-620 A/B Industrial-grade liquid silicone rubber for manufacturing construction molds is suitable for the molding and reproduction of large-scale stones, gypsum, cement parts, cultural stones, artificial stones, Roman columns, stone carvings and other furniture, construction and decoration products; it can also be used for
resin handicrafts, gypsum handicrafts, soap handmade soaps, tire turning molds, and other segmented molds.
Technical parameter of Tin Cure Silicone Rubber
| Model | HN-620AB |
| Feature | high temperature resistance |
| Viscosity (cs) | 170000 |
| Gravity ( G/cm 3 ) | 1.06 |
| Hardness(A°) | 20 |
| Strength( MPa) | 3.1-3.6 |
| Tear Strength (kN/m ) | 19.8-24.3 |
| Elongation(%) | 600-720 |
| Linear Shrinkage(%) | ≤0.2 |
| Curing Agent Addition Ratio(%) | 2-3% |
| Operating Time( mins ) | 30-40 |
| Curing Time( hours ) | 3-4 |
Feature of Tin Cure Silicone Rubber
1. Strong tear resistance, high and low temperature resistance, acid and alkali resistance, and aging resistance;
2. Good fluidity, easy to release foam, easy to demould, and the finished product will not turn white;
3. The silicone mold can be turned over frequently and has a long service life;
4. The linear shrinkage rate is less than two thousandths;
5. Product color, hardness, viscosity, and operating time can be adjusted as needed.
Feature
1 Two-component: liquid silicone rubber and curing agent
2. Good fluidity, easy foaming, easy perfusion
3. High-temperature resistance, acid and alkali resistance, low shrinkage
4. High tensile resistance, high tear resistance, many times of overturning
Product Tags:
|
|
Low Shrinkage Tin Cure Liquid Silicone Injection Molding Rubber Crafts Making HN-620 A/B Images
|